G10 Flange Insulation Gasket Kit
Fast Specifics
Product identify:3240 sheet, epoxy sheet, epoxy fiber glass sheet
Substance:epoxy resin + glass fiber Type:Insulation Components
Spot of Origin: China (Mainland) Brand Name:XIHU (WEST LAKE) DIS.
Model Quantity: 3240 fiberglass mat Type: fiberglass Insulation Sheet
Materials: Fiberglass Application: Large Voltage insulation materials
Rated Voltage: 10-one thousand kv Tensile Strength: 340MPa
Shade: Yellow Black Green or in accordance to customer’s requirm Density: two.08g/cm3
Thickness:.2-two.08mm Temp. Quality:: Class-F 155°C
Usage: B-Class Motor/Transformer Certification: CZPT:2000,ISO14001,UL,3C
Parallel bending strength: ≥33KJ/mthree Vertical electric powered strength: ≥9Kv
Parallel breakdown voltage: ≥35Kv Dielectric decline factor: ≤0.4
Surface area resistivity: ≥10 13Ω
Normal Size: 1571mmx 2040mm (40″ x 80″) or CZPT Sample: Sample Avaliable
3240 Epoxy glass fabric laminated sheet are created by modified phenolic
resin as binder and pure fiberglass as reinforcement. The have exceptionallygood warmth resistance and will not creep under large temperature conditions.
CZPT information
Flexural energy perpendicular to laminations: 340Mpa
Impact power parallel to laminations: 33kj/m2
Dielectric strength perpendicular to laminations: fourteen.2 MV/m
Breakdown voltage: 35kv
Density: one.8-two.08g/cm3
Thermal resistant: class F(155°c)
3240: Mechanical, electrical, electronic applications higher mechanical strength beneath average temperature, and very good electrical homes below large humidity.
CZPT info sheet
| Buy | Merchandise identify | Unit | Examination approach | Index |
| 1 | Density | g/cm3 | GB/T5130 section eight.1 | (1.80-2.08) |
| two | Drinking water absorption | mg | GB/T5130 section 8.two | Refer to table two |
| three | Vertical layer path bending energy | MPa | GB/T5130 part 5.1 | >= 340 |
| four | Vertical layer course compression energy | MPa | GB/T5130 area five.three | >= (350) |
| 5 | Tensile energy | MPa | GB/T5130 area 5.seven | >= (three hundred) |
| 6 | Compact toughness (Basically strut-beam technique) | KJ/mthree | GB/T5130 section 5.5.one | >= 33 |
| seven | Insulation resistance soon after drinking water dipping | Ω | GB/T5130 area 6.three | >= five. × 108 |
| 8 | Mediate decline aspect, 1MHz hour | ____ | GB/T5130 area 6.2 | <= 0.04 |
| nine | Dielectric continual, 1MHz hour | ____ | GB/T5130 area six.two | <= 5.5 |
| 10 | Vertical layer path electrical toughness at (90±2)ºC transformer oil | KV/mm | GB/T5130 section six.1 | Refer to desk three |
| 11 | Parallel layer course placing voltage | kV | GB/T5130 area 6.1 | >= 35 |
Complex PF FIBERGLASS EXPOXY SHEET
| NO | Merchandise | Unit | Index value | Remark |
| 1 | Vertical bending toughness | MPa | ≥340 | – |
| 2 | Parallel effect energy (just-supported beam approach) |
KJ/ | ≥33 | Possibly one conference this prerequisite is satisfactory. |
| three | Parallel influence power (cantilever beam approach) |
kJ/ | ≥34 | |
| four | Vertical electrical energy (in oil of 90ºC±2ºC,1mm) |
MV/m | ≥14.2 | – |
| five | Parallel breakdown voltage (in oil of 90ºC±2ºC) |
kV | ≥35 | – |
| 6 | Dielectric continuous (beneath 48Hz-62Hz) |
– | ≤5.five | – |
| 7 | Dielectric continuous (underneath 1MHz) |
– | ≤5.5 | |
| eight | Thermostability | ºC | 150 | – |
| 9 | Oil resistivity in transformer oil 4h | ºC | 130 | – |
| 10 | Tensile toughness lengthways horizontal | MPa | ≥314 ≥216 |
– |
| eleven | Adhesive power | N | ≥5600 | – |
| 12 | Dielectric dissipation element (underneath 48Hz-62Hz ) |
– | ≤0.04 | Possibly a single meeting this need is acceptable. |
| thirteen | Dielectric dissipation element (under 1MHz ) |
– | ≤0.04 | – |
| 14 | Density | g/ cm3 | (one.eight-two.08) | |
Technic Index Knowledge Sheet
| Properties | Device | Grade | |||
| Epoxy Glass Fabric Molded Rod | |||||
| 3840 | 3841 | 3841F | |||
| Flexural toughness | ≥ | MPa | 343 | 241 | 241 |
| Tensile toughness | ≥ | MPa | 196 | – | – |
| Compressive energy (Axial) | ≥ | MPa | – | 241 | 241 |
| Breakdown voltage parallel to laminations (in transformer oil) |
≥ | kV | 15 (90±2°C) |
15 (90±2°C) |
15 (90±2°C) |
| Insulation resistance parallel to lamination A: Beneath standard circumstances D-24/23: Immersion in drinking water |
≥ | W | one.0×1571 1.0×107 |
– – | – – |
| Density | g/cm3 | (1.70-1.ninety) | |||
| Drinking water absorption fee (D-24/23,25MM) |
≤ | % | – | .5 | .five |
| Flammability | Class | – | – | FV0 | |
| Color | – | All-natural | Inexperienced | Environmentally friendly | |
| Reference normal | – | Q/TXXFR004-2009 | |||
Epoxy glass cloth laminated sheets
Merchandise Description
EPGC201,EPGC202 board are from electrical alkali-free of charge glass cloth with epoxy resin Baptist,formed by sizzling urgent,Goods with higher mechanical houses and electrical efficiency.
EPGC201 epoxy glass fabric laminate used to B-class motors.electrical gear for insulation of structural areas.
EPGC202 epoxy glass fabric laminated sheets have flame-retardant requirements applicable to the B-class motors.electrical equipment for insulation of structural parts as other Needs.
Solution Description
EPGC203,EPGC204 plates are from 7628 glass cloth with epoxy resin Baptist,shaped by very hot urgent.Items with large mechanical homes.
EPGC203 epoxy glass fabric laminate used to F-course motors,electrical gear for insulation of structural components.
EPGC204 epoxy glass fabric laminated sheets have flame-retardant requirements applicable to the F-class motors,electrical equipment for insulation of structural areas.
CZPT parameters
| No | Product | Models | Indicators | ||||
| EPGC201 | EPGC202 | EPGC203 | EPGC204 | ||||
| 1 | Density | g/sqcm | one.seven-1.9 | one.7-1.nine | 1.8-2. | 1.8-2. | |
| two | Vertical layer to the bending toughness | Vertical | Mpa | 340 | 340 | 340 | 340 |
| Horizontal | Mpa | 250 | 250 | a hundred and seventy | 170 | ||
| 3 | Influence energy (merely supported beam approach,notched specimen) |
KJ/sqm | 37 | 37 | 34 | 34 | |
| four | Vertical Flammability | Quality | – | FV- | – | FV- | |
| 5 | Adhesive power | N | 6500 | 6500 | – | – | |
| 6 | Insulation Resistance | Regular | Ω | ||||
| Drinking water after 24h |
|||||||
| seven | Parallel to the layer high voltage ((90ºC+2ºC oil)) | KV | 35 | 35 | 5 | five | |
| eight | Vertical layers to the electrical power (90ºC+2ºC oil) | .five-1mm | MV/m | 20 | twenty | twenty | |
| 1.1-2mm | 18 | eighteen | 18 | eighteen | |||
| 2.1-3mm | sixteen | sixteen | 16 | 16 | |||
FAQ
Q1: How about MOQ?
MOQ is in accordance to various products. Whatsoever you require, we are happy to quote very best price with good top quality.
Q2: Can you send out samples for screening?
500g Samples are free equipped, but express freight must be taken by client. Right after generating order, we might like to return freight back.
Q3: How can you promise the good quality of mass goods is identical as the sample despatched to me ahead of?We held an additional very same sample and marked on company when we sent to buyer. So our production will be based mostly on.
This fall: Which deal do you use?
Package deal is essential element to steer clear of products breaking in transportation. We will choose appropriate packing depend on materials.Q5: When consumer react quality issues after decide up products, how to offer with?
1) CZPTer could offer photographs of issued goods for our income employees and then we are going to validate which portion is wrong.
two) If the issue is confirmed, firm will negotiate with customers and compensate in coming orders.
Packaging & Delivery
Packaging Particulars: Wood case Wood pallet or according to consumer requirments
Shipping and delivery Time: 10-20days right after receiving the deposit
You should Contact Us
Miss: lydia
Mob: 86~13 0571 88828 13858117778752439076 Fax: 86~571-8822571/8822 0571 -60863016
http://